| Title: | Influência das razões molares SiO2/Al2O3 e Me/Al2O3 sobre as propriedades de peneiras moleculares tipo SAPO-34 e MeAPSO-34 |
| metadata.dc.creator: | Carvalhal, Carlos Henrique de Melo |
| metadata.dc.contributor.advisor1: | Fernandes, Lindoval Domiciano |
| metadata.dc.contributor.referee1: | Fernandes, Lindoval Domiciano |
| metadata.dc.contributor.referee2: | Rodrigues, Alexandre Carlos Camacho |
| metadata.dc.contributor.referee3: | Martins, Renata Luz |
| metadata.dc.description.resumo: | A peneira molecular SAPO-34 foi sintetizada pelo método de cristalização hidrotérmica utilizando 4 valores diferentes para a razão molar SiO2/Al2O3 e 3 tempos de reações diferentes (24h, 48h e 120). A peneira molecularar MeAPSO-34 foi sintetizada pelo método de cristalização hidrotérmica utilizando 2 metais diferentes, níquel e cobalto, utilizando 5 razões molares Me/Al2O3 diferentes ( 0,0; 0,01; 0,02; 0,03 e 0,04). Todas as amostras de SAPO-34 e MeAPSO-34 obtidas foram caracterizadas por difração de raios-x, adsorção de nitrogênio, dessorção de amônia a temperatura programada e microscopia eletrônica de varredura. A análise de difração de raios-x confirmou a obtenção da estrutura tipo CHA para todos os casos. Por adsorção de nitrogênio foram obtidos valores de área específica e volume específico de microporo compatíveis com a estrutura esperada (CHA). Foi observado também que a acidez das amostras depende fortemente de sua composição química. |
| Abstract: | The molecular SAPO-34 was synthesized by hydrothermal crystallization method using 4 different values for the molar ratio SiO2/Al2O3 at 3 different reaction times (24h, 48h and 120). The molecular MeAPSO-34 was synthesized by hydrothermal crystallization method using two different metals, niquel and cobalt, using 5 molar ratio Me/Al2O3 different (0.0; 0.01; 0.02; 0.03 and 0.04 ). All samples of SAPO-34 and MeAPSO-34 obtained were characterized by X-ray diffraction, nitrogen adsorption, ammonia temperature programmed desorption and scanning electron microscopy. The analysis of X-ray diffraction confirmed the achievement of the CHA structure type in all cases. By nitrogen adsorption specific area were obtained, and values of specific micropore volume compatible with the expected structure (CHA). It was also observed that the acidity of the samples strongly depends on its chemical composition. |
| Keywords: | Catáilse Peneiras moleculares Olefinas Metanol |
| metadata.dc.subject.cnpq: | Engenharia Química |
| metadata.dc.language: | por |
| metadata.dc.publisher.country: | Brasil |
| Publisher: | Universidade Federal Rural do Rio de Janeiro |
| metadata.dc.publisher.initials: | UFRRJ |
| metadata.dc.publisher.department: | Instituto de Tecnologia |
| metadata.dc.publisher.program: | Programa de Pós-Graduação em Engenharia Química |
| Citation: | CARVALHAL, Carlos Henrique de Melo. Influência das razões molares SiO2/Al2O3 e Me/Al2O3 sobre as propriedades de peneiras moleculares tipo SAPO-34 e MeAPSO-34. 2015. 60 f. Dissertação (Mestrado em Engenharia Química). Instituto de Tecnologia, Universidade Federal Rural do Rio de Janeiro, Seropédica, RJ, 2015. |
| metadata.dc.rights: | Acesso Aberto |
| URI: | https://rima.ufrrj.br/jspui/handle/20.500.14407/11189 |
| Issue Date: | 19-Aug-2015 |
| Appears in Collections: | Mestrado em Engenharia Química |
Se for cadastrado no RIMA, poderá receber informações por email.
Se ainda não tem uma conta, cadastre-se aqui!
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| 2015 - Carlos Henrique de Melo Carvalhal.pdf | Documento principal | 5.57 MB | Adobe PDF |  View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.